(1)尺寸规格钢板和钢带的适用厚度范围为>4～60mm。其尺寸规格和允许偏差应符合GB／T709《热轧钢板和钢带》的规定。
(2)牌号和化学成分见表5-20。
表5-20优质碳素结构钢热轧厚钢板和宽钢带的牌号和化学成分
|
牌号
|
化学成分(质量分数)(％)
|
|||||||
|
C
|
si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Cu
|
|
|
≤
|
||||||||
|
05F
|
≤O．06
|
≤0.03
|
≤O．40．
|
O．035
|
0.040
|
O．10
|
O．25
|
0.25
|
|
08F
|
O．05～0.11
|
≤0.03
|
0.25～0.50
|
0.035
|
O．040
|
O．10
|
O．25
|
O.25
|
|
08
|
O．05～O．12
|
O．17～O．37
|
O．35～0.65
|
O．035
|
O．040
|
O．10
|
O，25
|
O．25
|
|
10F
|
0.07～O．14
|
≤O．07
|
0.25～0.50
|
O．035
|
O．040
|
O．15
|
O．25
|
0.25
|
|
10
|
O．07～0.14
|
O．17～O．37
|
0.35～O．65
|
O．035
|
0.040
|
O．15
|
O．25
|
O．25
|
|
15F
|
0.12～O．19
|
≤O．07
|
O．25～O．50
|
0.035
|
O．040
|
0.25
|
0.25
|
0.25
|
|
15
|
0.12～0.19
|
O．17～O．37
|
0.35～O．65
|
O．035
|
0.040
|
0.25
|
0.25
|
O．25
|
|
20F
|
O．17～O．24
|
≤O．07
|
O．25～O．50
|
O．035
|
0.040
|
0.25
|
0.25
|
0.25
|
|
20
|
O．17～O．24
|
O．17～O．37
|
O．35～0.65
|
O．035
|
O．040
|
O．25
|
O．25
|
0.25
|
|
25
|
O．22～O．30
|
0.17～O．37
|
0.50～O．80
|
0.035
|
0.040
|
O．25
|
0.25
|
O．25
|
|
30
|
0.27～O．35
|
O．17～0.37
|
O．50～O．80
|
O．035
|
0.040
|
0.25
|
O．25
|
0.25
|
|
35
|
0.32～O．40
|
O．17～O．37
|
0.50～O．80
|
O．035
|
O．040
|
0.25
|
0.25
|
0.25
|
|
40
|
O．37～0,45
|
0.17～O．37
|
O．50～O．80
|
0.035
|
O．040
|
0.25
|
0.25
|
0.25
|
|
45
|
O．42～O．50
|
0.17～0.37
|
0.50～0.80
|
0.035
|
0.040
|
0.25
|
O．25
|
O．25
|
|
50
|
O．47～O．55
|
0.17～O．37
|
0.50～O．80
|
O．035
|
O．040
|
O．25
|
0.25
|
0.25
|
|
55
|
O．52～O．60
|
O．17～O．37
|
0.50～0.80
|
O，035
|
O．040
|
O．25
|
0.25
|
O．25
|
|
60
|
O．57～O．65
|
O．17～O．37
|
O．50～O．80
|
0.035
|
O．040
|
O．25
|
0.25
|
O．25
|
|
65
|
0.62～O．70
|
0.17～O．37
|
O．50～O．80
|
O．035
|
O．040
|
0.25
|
0.25
|
O．25
|
|
70
|
O．67～0.75
|
0.17～0.37
|
0.50～O．80
|
O．035
|
0.040
|
O．25
|
O．25
|
O．25
|
|
20Mn
|
O．17～0.24
|
0.17～0.37
|
O．70～1.00
|
O．035
|
O．040
|
0.25
|
0.25
|
0.25
|
|
25Mn
|
0.22～0.30
|
0.17～0.37
|
O．70～1.00
|
0.035
|
0.040
|
O．25
|
O．25
|
0.25
|
|
30Mn
|
0.27～0.35
|
O．17～O．37
|
O．70～1.00
|
O．035
|
O．040
|
O．25
|
O．25
|
0.25
|
|
40Mn
|
0.37～O．45
|
0.17～O．37
|
0.70～1．00
|
O．035
|
O．040
|
0.25
|
0.25
|
O．25
|
|
50Mn
|
O．48～O．56
|
0.17～0.37
|
O．70～1．oo
|
O．035
|
0.040
|
O．25
|
0.25
|
O．25
|
|
60Mn
|
0.57～O．65
|
O．17～O．37
|
O．70～1.00
|
0.035
|
O．040
|
O．25
|
0.25
|
O．25
|
|
65Mn
|
0.62～0.70
|
O．17～0.37
|
O．90～1.20
|
0.035
|
O．040
|
0.25
|
O．25
|
0.25
|
注：1．08钢允许用铝代替硅脱氧。此时，钢中含锰量下限为0．25％，含硅量不大于0．03％，钢中酸溶铝AL含量为0．015％～0．065％或全铝ALt.含量为0．02％～0．07％，牌号为08Al。
2．上述含量皆指质量分数。